關 鍵 詞：ABS塑料，電鍍層，結合力，分析，控制 作 者： 內 容： 摘要：分析了ABS塑料在電鍍銅／鎳／鉻時鍍層出現起泡及終合力測試時鍍層脫落的主要原因，包括塑件基體狀態不良，注塑成型參數欠佳，電鍍前處理不當，相鄰鍍層表面活性差等。給出了提高ABS塑件鍍層結合力的措施，如選擇優質的電鍍鲴ABS塑料，控制成型工藝參數，改善前處理粗化及電鍍工序中的活化處理等。強調了采用正確的結合力測試方法的重要性。 關鍵詞：丙烯腈一丁二烯一苯乙烯共聚物；塑料；電鍍層；結合力；成型；前處理；測試方法 中圖分類號：TQl53．1 文獻標志碼：B 文章編號：1004—227X(2009)02—0013—03 Causes for poor adhesion strength of electroplated coating to ABS plastic and their controls／／WU Shui—gou Abstract：The main reasons for blistering of deposit durinl electroplating of Cu／Ni／Cr on ABS plastic and for fallin9—off of deposit in adhesion strength testing were analyzed．including unsatisfactory state of plastic substrate，unfavorabk injection molding parameters，improper pretreatment fol electroplating and insufficient surface activity of adjacenl deposits．Some measures for improving the adhesion strength of electroplated coating to ABS plastic were presented，such as selecting high—quality electroplating-grade ABS plastics，controlling molding process parameters，and improving the roughening process in pretreatment as well as the activating process in electroplatin9．The impogance oi using correct method for testing adhesion strength was emphasized． Keywords：poly(acrylonitrile—C0—butadiene—C0—styrene)；plastic；electroplated coatin9；adhesion strength；moldin9；pretreatment；test method Author’s address：Benli Plastic Plating Factory，Shenzhen 518105，China
1 前言
ABS塑料電鍍由簡單的裝飾用品已發展到高要求的電子、衛浴、汽車配件等工業領域。隨著市場的競爭，ABS塑料電鍍件的質量要求越來越高，尤其是物性測試中的鍍層結合力。因此，更多的ABS塑料電鍍廠家為保證塑件與電鍍層之間的結合力而采用自動電鍍生產線作業。由于ABS塑料工件品種多，注塑廠商為了降低成本，有時會選用品質較差的ABS塑料定型或采用不穩定的定型工藝注塑，而電鍍工藝又難以改變塑材因素對塑料鍍層結合力的影響，這一問題經常給ABS塑料電鍍一線操作人員帶來困擾，也給鍍層表面質量管理增添很多麻煩，直接影響用戶對產品的滿意程度，使企業質量管理及生產成本增加。筆者根據多年從事ABS塑料電鍍生產的實際經驗，針對鍍層與塑件間結合力差的缺陷進行了簡單分析，從選擇塑料、控制成型參數、加強電鍍工藝管理等方面出發，提出一些應對措施。
ABS塑料與電鍍層結合力差的原因分析及其控制：原因分析（一） ABS塑料與電鍍層結合力差的原因分析及其控制：原因分析（二） ABS塑料與電鍍層結合力差的原因分析及其控制：原因分析（三） ABS塑料與電鍍層結合力差的原因分析及其控制：原因分析（四） ABS塑料與電鍍層結合力差的原因分析及其控制：提高結合力措施 ABS塑料與電鍍層結合力差的原因分析及其控制：結論 注：本站部分資料需要安裝PDF閱讀器才能查看，如果你不能瀏覽文章全文，請檢查你是否已安裝PDF閱讀器！ |