中低溫化學鍍鎳工藝的新進展：前言

摘要：綜述了中低溫化學鍍鎳的常用方法，包括超聲波法、脈沖化學鍍法、加速催化法、電子載體法、有機酸配位劑法和光化學法。介紹了近年來該工藝的研究進展，總結了該領域的研究現狀并預測了發展方向。

關鍵詞：化學鍍鎳；中低溫；研究進展

中圖分類號；TQl53．12    文獻標志碼：A

文章編號：1004—227X(2009)05—0023—04 New development of the technology of middle and lowtemperature electroless nickel plating／／ZOU Jian-ping*LIU Xian-ze，XING Qiu-ju，WEI Da0—sheng，LIN Wan-feng，LIU Sheng·bin，LIANG Zhen，LI Guang—ming

Abstract：The commonly used methods of middle and lowtemperature electroless nickel plating were summarized，including plating assisted with ultrasonic and pulsed current，the addition of accelerators，electron carders and organic acid complexing agents，as well as photochemical methods．The recent research progress of the technology wasintroduced．The research status of the field was summed up and the development direction forecasted．

Keywords：electroless nickel plating；middle and lowtemperature；research progress

First-author’S address：School of Environment and Chemical  Engineering，  Nanchang Hangkong  University，Nanchang 330063，China

1  前言

    化學鍍鎳技術具有鍍層均勻，耐磨性、耐腐蝕性好，硬度高，操作方便等優點，適用于各種材料(包括非金屬材料)、復雜零件的施鍍，廣泛應用于石油、化工、汽車、電子、食品等領域。以硫酸鎳作為主鹽、次磷酸鹽作為還原劑的化學鍍液，通常分為酸性和堿性鍍液2種。堿性鍍液具有鍍速快、施鍍溫度低、能耗少、鍍層光亮度好等特點，但其穩定性較差，得到的化學鍍鎳層微結構通常是片狀的，微晶尺寸較大，晶粒間會產生孔隙甚至晶界；而酸性化學鍍鎳層是層狀或顆粒狀結構，可達到無孔隙，因而其耐磨性、耐蝕性以及硬度都比堿性化學鍍鎳層優越。因此，越來越多的研究者致力于酸性化學鍍鎳工藝的研究。目前，工業生產中普遍使用的鍍液的操作溫度為85～95 ℃，雖然鎳的沉積速率較快，但工藝控制困難，能耗高，設備耗損嚴重，勞動條件惡劣，鍍液易揮發、穩定性差、使用壽命短，次磷酸鹽的利用率低：另外，對于軟化點低和高溫下易變形的材料(如塑料等)，高溫操作會引起基體的變形和改性，因而限制了化學鍍鎳的進一步應用^[1-5]。

    降低化學鍍鎳的施鍍溫度，不僅可以降低施鍍成本，提高鍍液穩定性，而且便于加熱時控制溫度，方便現場施工操作^[6-7]。因此，中低溫化學鍍鎳工藝成為當前化學鍍領域的研究熱點課題。